Директното залепване магнезия хром тухла е изработена от високо-чистота синтетерирана магнезия и хром концентрат със SiO2< 2%="" as="" raw="" materials="" through="" high-temperature="" sintering.="" the="" direct="" bonding="" degree="" of="" the="" product="" increases="" with="" the="" reduction="" of="" sio2="" content="" and="" the="" increase="" of="" sintering="" temperature.="" the="" formation="" of="" direct="" bonding="" is="" a="" process="" of="" dissolution="" precipitation.="" increasing="" the="" content="" of="" fine="" powder="" of="" chromium="" concentrate="" is="" conducive="" to="" the="" formation="" of="" direct="" bonding.="" in="" the="" presence="" of="" silicate,="" the="" bonding="" between="" periclase="" and="" periclase="" will="" be="" strengthened="" by="" cr2o3,="" but="" reduced="" by="" al2o3="" and="" fe2o3.="" the="" higher="" the="" content="" of="" cr2o3,="" the="" more="" intragranular="" and="" intergranular="" spinels,="" the="" higher="" the="" strength="" of="" the="" product="" and="" the="" stronger="" the="" slag="">
Директно сближените магнезиеви хромирани тухли обикновено са разделени на различни степени на Cr2O3% ≥ 12% и Cr2O3 ≥ 20%, с ниска порьозност, висока якост, силна устойчивост на износване, добра устойчивост на корозия и добра устойчивост на разпростиране. Продуктите се използват широко в електрическите дъгови пещи, пещите за топене на мед, както и външните рафиниращи пещи